Industrial Paints & Protective Coatings

“We have your application covered”

New Steel

10-3 QD3 Quick Drying Black Eggshell Finish

Single pack, fast drying,rapid hardening, good adhesion
  • Overcoating Time @ 20°C : Should a second coat of QD3 be required, this must be applied within 2 hours of the first coat to avoid lifting or wrinkling of the QD3. After this 2 hour period, the QD3 will require at least 10 days curing before becoming resistant to solvents in the second coat.
  • Touch Dry @ 20°C: 15 minutes

120 Dacquacote Primer Finish

A water-borne acrylic coating for use as a primer for steel and similar substrates. Excellent adhesion and durability with rust-inhibitive properties. 'Environmentally Friendly'.  Typically applied to rolling stock and rail components

  • Overcoating Time @ 20°C : 4 hours with water-borne finishes. Note : To achieve the above drying times the paint film must be exposed to adequate air movement with good ventilation
  • Touch Dry @ 20°C: 20 minutes
  • Colour: Limited colour range available on request

13-3 Rapidac Matt Black

Single pack modified alkyd coating that is fast drying with a matt black industrial finish for use on mild steel components, wrought iron and similar applications.

  • Overcoating Time @ 20°C : May be overcoated when firm dry but within 1 hour or allow to dry overnight. Overcoating and drying times will depend on ambient temperatures and especially ventilation, air movement, etc.
  • Touch Dry @ 20°C: 20 minutes

150-462 Adhesion Promoter for Non Ferrous Metals

Aqueous emulsion galvanised steel, zinc, aluminium, stainless steel, copper, bronze etc. 
  • Overcoating Time @ 20°C : After 1-2 hours surfaces treated with adhesion promoter can be over coated with ALL types of paint eg epoxies, polyurethanes, vinyls, emulsions and alkyds.

200 Dac Sil 200 Poly Siloxane Gloss Finish

Single pack, high solids compliant, economical in use, fewer coats, lower applied cost. Excellent gloss and colour retention (1000 hrs QUV artificial exposure - no change. VOC compliant, isocyanate free, high abrasion resistance, excellent graffiti removal characteristics and good flexibility.

  • Overcoating Time @ 20°C : Not normally required
  • Touch Dry @ 20°C: 2-3 hours
  • Colour: Any BS4800/Ral/BS381C or bespoke colour

40 Low Odour Metal Primer

Single pack low odour primer with good adhesion and durability

  • Overcoating Time @ 20°C : Overnight
  • Touch Dry @ 20°C: 2 hours
  • Colour: Red Oxide or Grey

510 QD3 Quick Drying Gloss Enamel

Single pack modified alkyd fast drying gloss finish for general metal work. Rapid hardening with good adhesion

  • Overcoating Time @ 20°C : Should a second coat of QD3 be required, this must be applied within 2 hours of the first coat to avoid lifting or wrinkling of the QD3. After this 2 hour period, the QD3 will require at least 10 days curing before becoming resistant to solvents in the second coat
  • Touch Dry @ 20°C: 15 minutes
  • Colour: Tinted to any BS4800/Ral/BS381C or bespoke colour

524 Implamel One Coat Sheen Primer/Finish

Single pack general purpose 'one coat' primer/finish for structural steelwork, waste skips and similar steel fabrications.

  • Overcoating Time @ 20°C : Should a second coat be required, allow a minimum of 4 hours drying or preferably leave overnight between coats. The maximum over coating time is indefinite and is subject to normal good housekeeping practices for preparation an cleanliness between coats.
  • Touch Dry @ 20°C: 20 minutes
  • Colour: Tinted to any BS4800/Ral/BS381C or bespoke colour

579 Two Pack Epoxy Gloss Finish

Two pack, hard, abrasion and chemical resistant coating for harsh environments, outstanding resistance to alkalis and mild acids, oils, and hydrocarbon oil/solvents.

  • Overcoating Time @ 20°C : Overnight but within 5 days. (After 5 days, lightly abrade and solvent wipe.)
  • Touch Dry @ 20°C: 2 hours
  • Colour: Tinted to any BS4800/Ral/BS381C or bespoke colour

581 Two Pack Acrylic Gloss or Semi Gloss Finish

Two pack acrylic finish , excellent durability, colour and gloss retention, chemical resistance.  Isocyanate free.

  • Overcoating Time @ 20°C : Where a further coat of Acrylic Finish is required, this should be applied as soon as the first coat is touch-dry or, allow the first coat to dry for not less than 48 hours before overcoating.
  • Touch Dry @ 20°C: 1 hour
  • Colour: Tinted to any BS4800/Ral/BS381C or bespoke colour

585 Two Pack HS Polyurethane Gloss Finish

Two pack high solids polyurethane gloss finish, chemical resistant, excellent colour and gloss retention, compliant to Environmental Protection Act (1990) as required by Guidance Note PG6/23 (97), (Clause 20 (d).  Conforms to Highways Agency Specification Item 168.

  • Overcoating Time @ 20°C : N/A
  • Touch Dry @ 20°C: 2 hours
  • Colour: Tinted to any BS4800/Ral/BS381C or bespoke colour

591 UHB Tinted High Build Anti Corrosion Primer

Single pack or two pack high build primer (two pack when used with 591 GP Hardener/Activator)


  • Overcoating Time @ 20°C : 1 1/2 hours
  • Touch Dry @ 20°C: 10 minutes
  • Colour: Tinted to any BS4800/Ral/BS381C or bespoke colour

597 Vehicle & Machinery Gloss Enamel

Single pack modified alkyd finishing coat for vehicles, plant and machinery. Excellent durability with good resistance to oils, grease and similar. Dries to hard film with hard abrasion and impact resistance.

  • Overcoating Time @ 20°C : Should a second coat of Vehicle and Machinery Enamel be required, this can be applied as soon as the first coat is touch dry, ie. up to 1 hour - or allow coating to dry overnight.
  • Touch Dry @ 20°C: 1 hour
  • Colour: Tinted to any BS4800/Ral/BS381C or bespoke colour

599 Dacthane Gloss Enamel

Single pack  urethane alkyd finishing coat for vehicles, plant and machinery. Excellent durability with good resistance to oils, grease, etc. Dries to tough film with high abrasion and impact resistance.

Dacthane finishes from the Dacmix scheme are 'Compliant' to Environmental Protection Act (1990) Clause 20(d) of Guidance Note PG6/23 (97).

  • Overcoating Time @ 20°C : Should a second coat of Dacthane Enamel be required, this can be applied as soon as the first coat is touch dry, ie. up to 2 hours - or allow coating to dry completely for at least 16 hours.
  • Touch Dry @ 20°C: 2 hours
  • Colour: Tinted to any BS4800/Ral/BS381C or bespoke colour

78 Etch Primer

Single pack etch primer with modified zinc phosphate  inhibitive pigments.  Good adhesion to steel and non ferrous metals (aluminium, zinc, galvanising etc). Also used as a blast/holding primer for steel and as a sealer for aluminium and zinc metal spray.

  • Overcoating Time @ 20°C : After 90 minutes
  • Touch Dry @ 20°C: 5-10 minutes
  • Colour: White, Black, Grey
 