10-3 QD3 Quick Drying Black Eggshell Finish

• Overcoating Time @ 20°C : Should a second coat of QD3 be required, this must be applied within 2 hours of the first coat to avoid lifting or wrinkling of the QD3. After this 2 hour period, the QD3 will require at least 10 days curing before becoming resistant to solvents in the second coat.
• Touch Dry @ 20°C: 15 minutes

13 Rapidac High Build

Single pack high build quick drying zinc phosphate primer

• Overcoating Time @ 20°C : May be overcoated after 45 minutes or as soon as firm dry with Dacrylate Vehicle and Machinery Enamel or with Dacrylate QD3 Enamel when primer is firm dry but within 2 hours, or allow primer to dry overnight.
• Colour: Red Oxide, grey

510 QD3 Quick Drying Gloss Enamel

Single pack modified alkyd fast drying gloss finish for general metal work. Rapid hardening with good adhesion

• Overcoating Time @ 20°C : Should a second coat of QD3 be required, this must be applied within 2 hours of the first coat to avoid lifting or wrinkling of the QD3. After this 2 hour period, the QD3 will require at least 10 days curing before becoming resistant to solvents in the second coat
• Touch Dry @ 20°C: 15 minutes
• Colour: Tinted to any BS4800/Ral/BS381C or bespoke colour

524 Implamel One Coat Sheen Primer/Finish

Single pack general purpose 'one coat' primer/finish for structural steelwork, waste skips and similar steel fabrications.

• Overcoating Time @ 20°C : Should a second coat be required, allow a minimum of 4 hours drying or preferably leave overnight between coats. The maximum over coating time is indefinite and is subject to normal good housekeeping practices for preparation an cleanliness between coats.
• Touch Dry @ 20°C: 20 minutes
• Colour: Tinted to any BS4800/Ral/BS381C or bespoke colour

541 Vinadac High Build Vinyl Sheen

Single pack fast drying high build vinyl pigmented with light fast durable pigmentation. High build coating for protection of steel and galvanised steel in aggressive environments.  Tolerant of damp surfaces during application with excellent flexibility retention.

• Overcoating Time @ 20°C : 3 hours
• Touch Dry @ 20°C: 2 hours
• Colour: Tinted to any BS4800/Ral/BS381C or bespoke colour

547 SB Acrylic Vinyl Sheen Finish

Single pack fast drying high build acrylic vinyl pigmented with durable, light fast pigments offering excellent durability and colour retention properties.  Suitable for application to plastisol, uPVC and other such substrates.  Long term durability up to 10 years.

• Overcoating Time @ 20°C : 3 hours
• Touch Dry @ 20°C: 1 hour
• Colour: Tinted to any BS4800/Ral/BS381C or bespoke colour

579 Two Pack Epoxy Gloss Finish

Two pack, hard, abrasion and chemical resistant coating for harsh environments, outstanding resistance to alkalis and mild acids, oils, and hydrocarbon oil/solvents.

• Overcoating Time @ 20°C : Overnight but within 5 days. (After 5 days, lightly abrade and solvent wipe.)
• Touch Dry @ 20°C: 2 hours
• Colour: Tinted to any BS4800/Ral/BS381C or bespoke colour

581 Two Pack Acrylic Gloss or Semi Gloss Finish

Two pack acrylic finish , excellent durability, colour and gloss retention, chemical resistance.  Isocyanate free.

• Overcoating Time @ 20°C : Where a further coat of Acrylic Finish is required, this should be applied as soon as the first coat is touch-dry or, allow the first coat to dry for not less than 48 hours before overcoating.
• Touch Dry @ 20°C: 1 hour
• Colour: Tinted to any BS4800/Ral/BS381C or bespoke colour

585 Two Pack HS Polyurethane Gloss Finish

Two pack high solids polyurethane gloss finish, chemical resistant, excellent colour and gloss retention, compliant to Environmental Protection Act (1990) as required by Guidance Note PG6/23 (97), (Clause 20 (d).  Conforms to Highways Agency Specification Item 168.

• Overcoating Time @ 20°C : N/A
• Touch Dry @ 20°C: 2 hours
• Colour: Tinted to any BS4800/Ral/BS381C or bespoke colour

591 UHB Tinted High Build Anti Corrosion Primer

Single pack or two pack high build primer (two pack when used with 591 GP Hardener/Activator)

• Overcoating Time @ 20°C : 1 1/2 hours
• Touch Dry @ 20°C: 10 minutes
• Colour: Tinted to any BS4800/Ral/BS381C or bespoke colour

597 Vehicle & Machinery Gloss Enamel

Single pack modified alkyd finishing coat for vehicles, plant and machinery. Excellent durability with good resistance to oils, grease and similar. Dries to hard film with hard abrasion and impact resistance.

• Overcoating Time @ 20°C : Should a second coat of Vehicle and Machinery Enamel be required, this can be applied as soon as the first coat is touch dry, ie. up to 1 hour - or allow coating to dry overnight.
• Touch Dry @ 20°C: 1 hour
• Colour: Tinted to any BS4800/Ral/BS381C or bespoke colour

599 Dacthane Gloss Enamel

Single pack  urethane alkyd finishing coat for vehicles, plant and machinery. Excellent durability with good resistance to oils, grease, etc. Dries to tough film with high abrasion and impact resistance.

Dacthane finishes from the Dacmix scheme are 'Compliant' to Environmental Protection Act (1990) Clause 20(d) of Guidance Note PG6/23 (97).

• Overcoating Time @ 20°C : Should a second coat of Dacthane Enamel be required, this can be applied as soon as the first coat is touch dry, ie. up to 2 hours - or allow coating to dry completely for at least 16 hours.
• Touch Dry @ 20°C: 2 hours
• Colour: Tinted to any BS4800/Ral/BS381C or bespoke colour

7-610

Single pack fast dry synthetic topcoat.  High gloss for plant and agricultural machinery.

79-458 Epidac 2 High Build Zinc Phosphate Primer

Two pack high build epoxy with anti corrosion pigmentation for use on prepared steel and galvanised steel.

Fully compliant to Environmental Protection Act (1990) as required by Guidance Note PG 6/23 (97), Clause 20 (d), when used as tie coat, sealer or blast primer.

• Overcoating Time @ 20°C : Overnight
• Touch Dry @ 20°C: 2-4 hours
• Colour: Grey

79-498 Epidac 2 High Build Fast Set Epoxy Primer

Two pack FAST SET high build  zinc phosphate epoxy primer reinforced with micaceous  iron oxide pigmentation.

For use on prepared steel and galvanised surfaces especially where rapid overcoating is required. Typical applications include lighting columns and general industrial plant. For site maintenance where rapid curing is an advantage.

• Overcoating Time @ 20°C : 2 hours (single pack) / 1 hour (two-pack)
• Touch Dry @ 20°C: 30 minutes
• Colour: Grey